Damage predictions for the 2024-T351 aluminium alloy under both monotonic and cyclic loadings

KONDEPATI, S. ADAMEC, T. HASSAN, T. ŠEBEK, F.

Anglický název

Damage predictions for the 2024-T351 aluminium alloy under both monotonic and cyclic loadings

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

en

Originální abstrakt

The failure behaviour is investigated for the 2024-T351 aluminium alloy subjected to monotonic and cyclic loading conditions using the void growth model. Notched cylindrical specimens are employed to analyse the behaviour under monotonic loading, while smooth cylindrical specimens are used for cyclic loading. The analysis encompasses a broad spectrum, ranging from the ultra-low cycle fatigue regime to the low-cycle fatigue. This comprehensive approach aims to provide a thorough understanding of fracture behaviour across a wide range of loading severities.

Anglický abstrakt

The failure behaviour is investigated for the 2024-T351 aluminium alloy subjected to monotonic and cyclic loading conditions using the void growth model. Notched cylindrical specimens are employed to analyse the behaviour under monotonic loading, while smooth cylindrical specimens are used for cyclic loading. The analysis encompasses a broad spectrum, ranging from the ultra-low cycle fatigue regime to the low-cycle fatigue. This comprehensive approach aims to provide a thorough understanding of fracture behaviour across a wide range of loading severities.

Klíčová slova anglicky

Cyclic loads

Vydáno

07.07.2025

ISSN

1742-6588

Kniha

COMAT-2024

Ročník

3035

Číslo

1

Strany od–do

1–6

Počet stran

6

BIBTEX


@inproceedings{BUT198469,
  author="Sudhir Kumar {Kondepati} and Tomáš {Adamec} and Tasnim {Hassan} and František {Šebek},
  title="Damage predictions for the 2024-T351 aluminium alloy under both monotonic and cyclic loadings",
  booktitle="COMAT-2024",
  year="2025",
  volume="3035",
  number="1",
  month="July",
  pages="1--6",
  issn="1742-6588"
}